Phynox® is a Cobalt-Chrome-Nickel alloy which is capable of very high strength levels (330ksi) after cold forming and aging. This alloy is the material of choice for many medical applications due to its high fatigue resistance as well as being biocompatible, non-magnetic and suitable for implants.
Applications
Joint replacement
Medical, surgical, dental instruments
Stents, lines
Drill lines
Watch components
Aerospace industry
Micro-engineering
Typical Chemical Composition
| C | Si | Mn | P | S | Cr | Mo | Ni | Be | Co | Fe | |
| Min | 1.50 | 19.00 | 6.00 | 14.00 | 39.00 | ||||||
| Max | 0.15 | 2.50 | 21.00 | 8.00 | 16.00 | 0.1 | 41.00 | Balance |
Typical Mechanical Properties
| Condition | Tensile (Rm) KSI |
Yield (R0.2%) KSI |
Hardness HRC |
||||
| Solution Heat Treated / Cold Drawn | 220-260 | NA | NA | ||||
| Solution Heat Treated / Cold Drawn / Aged | 270-330 | 180-210 | 46 | ||||
Specifications
2.4711
AFNOR K13C20N16Fe15D07
ASTM F1058
AMS 5833 / AMS 5834
ISO 5832-7
UNS R30003
UNS R30008
Availability
Phynox® (2.4711) is available in wire and round bar from 0.200mm diameter up to 15.00mm diameter