Alloy MP35N® is a Vacuum Induction Melt / Vacuum Arc Remelt (VIM/VAR) cobalt alloy which obtains very high strength, corrosion resistance and fatigue resistance due to its two-stage cold working and aging treatment process. Machining is relatively difficult and not advised in the annealed condition so material is supplied in the solution treated and cold worked condition to allow for the final ageing stage. After aging, hardness levels can reach over 55 HRC and strengths levels as high as 260-300ksi.
Applications
Orthopedic implants
Joint replacement
Medical, surgical, dental instruments
Watch components
Aerospace industry
Micro-engineering
Typical Chemical Composition
| C | Si | Mn | P | S | Cr | Mo | Ni | Fe | Co | |
| Min | 19.00 | 9.00 | 33.00 | |||||||
| Max | 0.02 | 0.15 | 0.15 | 0.015 | 0.010 | 21.00 | 10.50 | 37.00 | 1 | Balance |
Typical Mechanical Properties
| Condition | Tensile (Rm) KSI |
Yield (R0.2%) KSI |
Elongation A4d (%) |
Reduction of Area % |
Hardness HRC |
||||
| Solution Heat Treated / Cold Worked | 255 | 225 | 12 | 50 | 45 | ||||
| Solution Heat Treated / Cold Worked / Aged | 260 | 230 | 8 | 35 | 38 min | ||||
Specifications
2.4782
ASTM F562
ISO 5832-6
AMS 5758
AMS 5844
AMS 5845
UNS R30035
Availability
Alloy MP35N® is available in wire and round bar from 0.600mm diameter up to 35.00mm diameter