Stainless steel grade 465 is a premium, Vacuum Induction Melted and Vacuum Arc Remelted steel capable of very high tensile strength, fracture toughness and resistance to stress corrosion cracking. Supplied in the solution annealed condition, it has improved machinability characteristics compared to similar alloys
Applications
Medical instruments
Drill bits
Agro-food industries
Typical Chemical Composition
| C | Si | Mn | P | S | Cr | Mo | Ni | Ti | Fe | |
| Min | 11.00 | 0.75 | 10.75 | 1.5 | ||||||
| Max | 0.02 | 0.25 | 0.25 | 0.015 | 0.010 | 12.50 | 1.25 | 11.25 | 1.8 | Balance |
Typical Mechanical Properties
| Condition | Tensile (Rm) KSI |
Yield (R0.2%) KSI |
Elongation A4d (%) |
Reduction of Area % |
Hardness HRC |
| Sol Annealed | ≤160 | 20 | 75 | ≤331 HB | |
| H950 | 240 | 220 | 10 | 45 | 47 |
| H1000 | 220 | 200 | 10 | 50 | 45 |
Heat Treatment of Custom 465
Solution Treatment : 1800 °F ± 25 (982 °C ± 14), holding 60 minutes (± 15) + quenching in oil or water Then cooling to -100 °F (-73 °C) or colder, holding at that temperature for not less than eight hours, and warming in air to room temperature.
H950 : 950°F ± 10 (510°C ± 6), holding 4 hours (± 0.3) + air/oil/water quench
H1000 : 1000°F ± 10 (538°C ± 6), holding 4 hours (± 0.3) + air/oil/water quench
Specifications
UNS S46500
1.4614
ASTM A564
ASTM F899
ASTM F1537 Alloy 1
AMS 5936 Cap of H1000
Availability
Stainless Steel Custom 465 is available in round bar from 1.50mm diameter up to 107.95mm diameter