Grade 4 (ASTM F67) is a commercially pure titanium alloy, produced via Vacuum-Arc-Melting and Remelting, giving close control over its C, O, N, H and Fe contents. The alloy can be cold formed to give high strength levels without impairing the final ductility. It is has an excellent biocompatibility with the human
Applications
Implants
Medical instruments
Dental instruments and applications
Surgical applications
Micro-engineering
Watch-making
Typical Chemical Composition
C | Fe | O | N | H | Ti | |
Min | ||||||
Max | 0.08 | 0.50 | 0.40 | 0.05 | 0.0125 | Balance |
Typical Mechanical Properties
Condition | Tensile (Rm) Mpa |
Yield (R0.2%) Mpa |
Elongation A4d (%) |
Annealed | 800-900 | 620 | 10 |
Cold worked | 930-1135 | 655-825 |
Specifications
3.7065
EN/DIN Ti-4
ISO 5832-2
AFNOR T60
ASTM B348
ASTM F67
UNS R50700
Availability
Titanium Grade 4 (3.7065) is available in wire and round bar from 1.50mm diameter up to 35.00mm diameter